LITHIUM GREASE WITH A HIGH MoS2 CONTENT
EXTREME PRESSURE, ANTI-WEAR,
ANTI-CORROSION, ANTI-PITTING, ANTI-FRETTING
FOR RELIABLE LUBRICATION
THAT IS EXTREMELY LONG-LASTING
REDUCES LUBRICATION FREQUENCY
DESCRIPTION
Grease with a high MoS2 content, suited to all general lubrication issues, in particular for use on plain and ball bearings.
Easy resolution of wear and heating problems, while lengthening lubrication intervals.
The submicronised solid lubricant particles provide effective protection of surfaces, in case of accidental rupture of the lubricating film, in a hydrodynamic system.
Neolube® GR 140 is remarkably stable , does not harden, can be easily pumped, and is suitable for use in centralised automatic lubrication systems.
AREAS OF USE
General mechanical use, machine tools, auto mechanics, civil engineering, mines/pits, the steel industry, agricultural equipment.
Long-term lubrication of radio tribocontact ball bearings, roller bearings, taper roller bearings, needle roller bearings, open pinions.
Surface tribocontacts, plain bearings, joint bearings, cardans, bearing pins, worm gears, guidance systems, slide rails.
TYPICAL PHYSICO-CHEMICAL PROPERTIES
|
PHYSICAL PROPERTIES OF THE GREASE |
|||
|
PROPERTIES |
STANDARD OR METHOD |
VALUE |
UNIT |
|
Appearance |
visual |
smooth |
nm |
|
Colour |
in |
black |
nm |
|
Apparent density at 25°C/77°F (pycnometer) |
NF T 30 020 |
865 |
kg/m³ |
|
NLGI Class |
NLGI National Lubricating Grease Institute |
2 |
Classification |
|
Thickener |
- |
Lithium |
- |
|
Solid lubricant content |
- |
MoS2<10µ |
>3% |
|
Penetrability at 25°C/77°F Non-worked Worked, 60 strokes Worked, 1,000 strokes Worked, 10,000 strokes Worked, 100,000 strokes |
NF ISO 2137 / ASTM 2176
|
265-295 265-295 265-295 275-305 280-310 |
1/10° mm 1/10° mm 1/10° mm 1/10° mm 1/10° mm |
|
Dropping point Dropping point if greater than 360°C/680°F |
NF ISO 2176 / ASTM D 566 ASTM D 2265 |
>180 >356
|
°C °F |
|
Impurities > 25 µm > 75 µm > 125 µm |
FMTS 791 3005 |
0 0 0 |
nb/ml |
|
PHYSICO-CHEMICAL PROPERTIES OF THE BASE OIL |
|||
|
PROPERTIES |
STANDARD OR METHOD |
VALUE |
UNIT |
|
Type of base oil |
- |
Mineral |
- |
|
Kinematic viscosity at 40°C/104°F Kinematic viscosity at 100°C/212°F |
NF EN ISO 3104 |
140 110 |
mm2/s mm2/s |
|
Acid value (AV) |
NF ISO 6618 |
0.5 |
mg KOH/l |
|
PERFORMANCE PROPERTIES |
|||
|
PROPERTIES |
STANDARD OR METHOD |
VALUE |
UNIT |
|
Oil separation, 7 days at 40°C/104°F (bleeding) |
NF T 60 191 |
0 |
% of mass |
|
Oil separation 24 hours at 41 kPa (bleeding under pressure) |
ASTM D 1742 |
4 |
% of mass |
|
Sulphated ashes |
NF T 60 144 |
5 |
% of mass |
|
Copper strip corrosion |
ASTM D 4048 |
1b |
Rating |
|
Hoffman oxidation |
ASTM D 942 |
40 |
psi |
|
Loss by evaporation 22 hours at 121°C/249,8°F |
ASTM D 972 |
2 |
% of mass |
|
Noack evaporation loss |
NF T 60 101 CEC L-40 A-93 ASTM D5800 |
3 |
% of mass |
|
Elastomer swelling 70h at 100°C/212°F |
ASTM D 4289.83 |
0.8 |
Dimensional variation % |
|
Temperature ranges Continuous Peak |
- - |
-20°C +140°C/-4°F +284°F -20°C +150°C/-4°F +302°F |
- |
|
Rotation factor |
n.dm |
500,000 |
mm/min-1 |
|
4-ball test Wear scar diameter Wear load index |
ASTM D 2266 / ISO 20 623 |
0.65 3500 |
mm N |
|
TIMKEN Test |
ASTM D 2509 |
45 |
lbs |
|
EMCOR rust prevention test Dynamic Static |
NF T 60 135 ISO DP 6294/ ASTM D 1743 |
2 2 |
Rating Rating |
|
Resistance to water washout at 80°C/176°F |
ASTM 1264 |
8 |
% of mass |
* not measured or non-measurable
PRESENTATIONS
|
1 L Tin
|
430 ml Cartridge
|
Looking for another product?
|
Discover our entire range by clicking on the photo |
Manufacturing, lubrification, cleansing, protection,
IBiotec® Tec Industries® Service
offers a wide range of products reserved for industrial area
If you wish for :
a free sample
a technical advice